There is a concern regarding sub-surface pores within laser powder bed fusion of Ti-6Al-4V, which can initiate cracks and reduce mechanical properties, especially after machining for surface finishing. This study investigated the effect of laser scanning speed and fine shot peening on the pore characteristics, hardness, and residual stress of Ti-6Al-4V fabricated by laser powder bed fusion using scanning electron microscopy, X-ray micro-computed tomography, Vickers hardness, and X-ray diffraction. As the laser scanning speed increased, the number of pores and pore size increased, which reduced the hardness of Ti-6Al-4V. Most pores were less than 20 µm in size and randomly distributed. The fine shot peening generated plastic deformation and compressive residual stress on the surface, leading to higher hardness, with similar surface properties at all scanning speeds. The depth of compressive residual stress by fine shot peening varied corresponding to the scanning speeds. Increasing the scanning speed accelerated the rate of conversion between the compressive and tensile residual stresses, and decreased the depth of the maximum hardness by the fine shot peening from initial tensile residual stress within Ti-6Al-4V fabricated by laser powder bed fusion, thus reducing the enhancement achieved by the fine shot peening.