Many of the peculiar properties of the vasculature are related to the arrangement of anisotropic proteinaceous fibers in vessel walls. Understanding and imitating these arrangements can potentially lead to new therapies for cardiovascular diseases. These can be pre‐surgical planning, for which patient‐specific ex vivo anatomical models for endograft testing are of interest. Alternatively, therapies can be based on tissue engineering, for which degradable in vitro cell growth substrates are used to culture replacement parts. In both cases, materials are desirable that imitate the biophysical properties of vessels, including their tubular shapes and compliance. This work contributes to these demands by offering methods for the manufacturing of anisotropic 3D‐printed nanofibrous tubular structures that have similar biophysical properties as porcine aortae, that are biocompatible, and that allow for controlled nutrient diffusion. Tubes of various sizes with axial, radial, or alternating nanofiber orientation along the blood flow direction are manufactured by a customized method. Blood pressure‐resistant, compliant, stable, and cell culture‐compatible structures are obtained, that can be degraded in vitro on demand. It is suggested that these healthcare materials can contribute to the next generation of cardiovascular therapies of ex vivo pre‐surgical planning or in vitro cell culture.

3D printing of bio‐based nanomaterials into complex structures with design flexibility, structural anisotropy, and long‐term stability is a key issue for biomedical applications. Herein, 3D‐printed and ionically crosslinked structures with anisotropic, water‐proof, and tunable mechanical properties are fabricated using a polysaccharide ink composed of nanocellulose, alginate, and CaCO 3 nanoparticles. The excellent shear thinning properties of the ink, combined with double or even triple extrusion, allow printing of complex structures (tubes, buckets, ears, and boat models) with high shape fidelity even after crosslinking. The anisotropically printed and crosslinked structures can be mechanically tuned by controlling the fiber orientation via the printing path, the amount of crosslinker, the type of acid used for crosslinking (weak to strong), and the storage medium. This allows for tailored flexibility and a tensile modulus of the materials in wet state ranging from 1 to 30 MPa. Application of hydrostatic pressure of 160–600 mmHg for 24 h with a physiological fluid to a tubular structure, a model for the cardiovascular system, shows no leakage or rupture in the tube. The great design freedom offered by 3D printing and spatially controlled structural anisotropy enable the production of tailored materials for soft robotics or biomedical applications.