316L stainless steel joined to mild steel is widespread in several applications to reach a requested good association of mechanical properties at a lower cost. The activating tungsten inert gas (ATIG) weld was carried out using a modified flux composed of 76.63% SiO2 + 13.37% Cr2O3 + 10% NaF to meet standard recommendations in terms of limiting the root penetration. Modified optimal flux gave a depth of penetration 1.84 times greater than that of conventional tungsten inert gas (TIG) welds and a root penetration of up to 0.8 mm. The microstructure of the dissimilar joints was investigated using a scanning electron microscope and EDS analysis. The mechanical properties of the weld were not affected by the modified flux. The results show that the energy absorbed in the fusion zone in the case of ATIG weld (239 J/cm2) is greater than that of TIG weld (216 J/cm2). It was found that the weld bead obtained with the optimal flux combination in ATIG welding can better withstand sudden loads. The obtained UTS value (377 MPa) for ATIG welding was close to that of TIG welding (376 MPa). The average Vickers hardness readings for ATIG welds in the fusion zone are up to 277 HV, compared to 252 HV for conventional TIG welding.