Agnieszka Wdowiak-Postulak

In addition to traditional building materials, such as steel and concrete, wood has been gaining increasing prominence in recent years. In the past, the use of wood was limited due to its susceptibility to damage by fungi, insects, and temperature. These shortcomings were gradually eliminated as the quality of wood processing increased and thanks to modern high-quality insulating and protective materials. The return to the utilisation of this natural building material was also supported by the development of new wood-based materials, such as glued laminated wood, and new types of mechanical fasteners, as well as by the introduction of new design methods provided in the Eurocodes. Within this context, this paper focuses on using wood in transport infrastructure, especially as the basic material for footbridges and small road bridges. Combined timber–steel bridges emerge as a very effective type of superstructure in contemporary road bridges and footbridges, especially in areas with natural exposure. Usually, wood is used for the main bridge girders, while steel is preferred for bridge deck elements—stringers and cross-girders. The results of this parametric study offer optimal structural solutions for footbridges with spans of 12.0–24.0 m, reflecting satisfactory static and dynamic footbridge behaviour. Particular attention is paid to a problematic structural detail—the connection between the steel cross-girder and the timber main girder. Firstly, this connection’s characteristics were measured experimentally using nine laboratory samples made of two glued laminated timber blocks, simulating main girders connected with a hot-rolled steel cross-girder. The connection was prepared in three variants, with different heights of the end plates and different numbers of bolts. Subsequently, these characteristics were computed using two numerical FEM models. The first model was created using SCIA Engineer software with a combination of shell and beam finite elements. The second, more sophisticated model was created in the ANSYS software environment using 3D finite elements, allowing us to better take into account the plasticity and orthotropic properties of wood and the points of contact between the individual members. Finally, the experimental results produced by sample testing in the laboratory were compared to the outputs of FEM numerical studies.

These elements are innovative and of interest to many researchers for the reinforcement of wooden elements. For the reinforced beam elements, the effect of the reinforcement factor, FRP and steel elastic modulus or FRP and steel arrangement of the reinforcement on the performance of the flexural elements was determined, followed by reading the load-displacement diagram of the reinforced beam elements. The finite element model was then developed and verified with the experimental results, which was mainly related to the fact that the general theory took into account the typical tensile failure mode, which can be used to predict the flexural strength of reinforced timber beams. From the tests, it was determined that reinforced timber beam elements had relatively ductile flexural strengths up to brittle tension for unreinforced elements. As for the reinforcements of FRP, the highest increase in load-bearing capacity was for carbon mats at 52.47%, with a reinforcement grade of 0.43%, while the lowest was for glass mats at 16.62% with a reinforcement grade of 0.22%. Basalt bars achieved the highest stiffness, followed by glass mats. Taking into account all the reinforcements used, the highest stiffness was demonstrated by the tests of the effectiveness of the reinforcement using 3 mm thick steel plates. For this configuration with a reinforcement percentage of 10%, this increase in load capacity was 79.48% and stiffness was 31.08%. The difference between the experimental and numerical results was within 3.62–27.36%, respectively.

Damage often develops in glued laminated timber members under high bending loads due to natural defects in the timber, which results in their low load-bearing capacity and stiffness. In order to improve the bending mechanical properties of glulam beams, a new type of longitudinal glulam reinforcement with pre-stressed basalt fibre-reinforced polymer composites (BFRP) was developed using the Near Surface Mounted (NSM) technique. The strengthening method consisted of two pre-stressed BFRP bars glued into the grooves at the bottom side of the beam; meanwhile, for the second strengthening alternative, the third BFRP bar was embedded into the groove at the top side of the beam. Therefore, an experimental study was carried out to verify this strengthening technique, in which fifteen full-size timber beams were tested with and without bonded BFRP bar reinforcement in three series. According to the results of this experimental study, it can be seen that the effective load-bearing capacity of the reinforced beams increased up to 36% and that the stiffness of the beams increased by 23% compared to the unreinforced beams. The tensile stresses in the wooden fibres were reduced by 11.32% and 25.42% on average for the beams reinforced with two and three BFRP bars, respectively. On the other hand, the compressive stresses were reduced by 16.53% and 32.10% compared to the unreinforced beams. The usual failure mode saw the cracking of the wood fibres at the defects, while for some specimens, there were also signs of cracks in the epoxy adhesive bond; however, the crack propagation was, overall, significantly reduced. The numerical calculations also show a good correlation with the experimental results. The difference in the results between the experimental and numerical analysis of the reinforced and unreinforced full-sized beams ranged between 3.63% and 11.45%.