In this work, the performances of nickel iron layered double hydroxides (LDH) with the nitrate anion at the interlayer (NiFe-NO3) for the manufacture of anodes for lithium-ion batteries have been tested before and after its sintering at different temperatures. After synthesis, the material was thermally analyzed in a range 30–1250 °C, showing a mass loss occurring in three different consecutive steps leading to a total mass decrease of ~30 mass%. Following thermogravimetric analysis (TGA), four samples were prepared by annealing at four different temperatures: one of the four did not undergo a thermal treatment (NiFe-0), while the remaining three were annealed at 250 °C, 360 °C, and 560 °C for 6 h (NiFe-250, NiFe-360, and NiFe-560). All materials where completely characterized via FE-SEM, PXRD, and FT-IR. The pristine LDH material showed some structural and compositional changes for growing temperatures, starting from the typical turbostratic hexagonal structure through a mixture of amorphous metal oxides and finally to the stoichiometric oxides FeNi2O4 and NiO. The as-obtained materials were mixed with carbon black (C65) and sodium alginate and tested as electrodes in Swagelok half cells in LP30 vs. metallic Li to perform CV and GCPL analysis. The electrochemical tests showed that the performances of NiFe-0, both in terms of stability and specific capacity, are not so different from the one of the NiFe-560, even if the Ni mass% in the former is lower than in the NiFe-560. This phenomenon could be explained by assuming a combined mechanism of reaction involving both intercalation and conversion.

Within the framework of the various strategies studied for the abatement of polluting agents in water, both from anthropogenic and natural origins, adsorption processes are among the most widespread techniques. In this context, Layered Double Hydroxides (LDHs) play a fundamental role. In this study, a Mg–Al LDH (nitrate intercalated, Mg/Al = 2) was prepared to be used as an anion exchanger for Cr(VI)-removal purposes from water. The LDH was synthesized through a coprecipitation reaction, followed by an aging process under heating. The compound was characterized by means of inductively coupled plasma–atomic emission spectroscopy (ICP-AES), X-ray powder diffraction (XRPD), field-emission scanning electron microscopy (FE-SEM) and Fourier-transform infrared spectroscopy (FT-IR). Regarding LDH adsorption capacity, with respect to Cr(VI), the adsorption isotherms and reaction kinetic were studied, and the adsorption process was well described by the Langmuir model. A central composite design was used for the multivariate optimization of the working parameters. The maximum adsorption capacity was estimated to be 30 mg/g.