Introduction: We compared the effects of heat on the physicochemical properties of recently developed calcium silicate-based sealers (CSBSs), including BioRoot Flow, BioRoot RCS, and AH Plus Bioceramic sealer, with those of the epoxy-resin-based sealer (ERBS) AH Plus. Methods: The flow, film thickness, setting time, and solubility of sealers were evaluated at 37 °C and 100 °C using ISO 6876/2012. Furthermore, pH and calcium ion release were evaluated at these temperatures. In addition, the mass change in sealers at a high temperature was assessed via thermogravimetric analysis. Then, the chemical composition and components of the sealers were analyzed using a scanning electron microscope and Fourier-transform infrared spectroscopy (FTIR). Results: BioRoot Flow, AH Plus Bioceramic, and AH Plus complied with ISO standards in terms of flow and film thickness, both before and after heat application. However, BioRoot RCS exhibited significantly increased film thickness at 100 °C. The setting times of all sealers were significantly reduced at 100 °C. The solubility of CSBS was >3%, exceeding the ISO 6876/2012 standard, both before and after heat exposure. Conversely, the solubility of AH Plus complied with the standard, regardless of the thermal condition. For 4 weeks, CSBS showed a significantly higher pH than AH Plus at both 37 °C and 100 °C. After heat treatment, calcium release decreased in Bioroot RCS and BioRoot Flow, while AH Plus showed no significant differences before and after treatment. However, CSBS consistently exhibited significantly higher calcium release than AH Plus at both temperatures. An FTIR analysis revealed that the chemical composition of the sealers did not change at the high temperature, whereas a thermogravimetric analysis demonstrated a >5% weight reduction in CSBS and a 0.005% weight reduction in AH Plus at 100 °C. Conclusions: BioRoot Flow, AH Plus Bioceramic, and AH Plus possess favorable physicochemical properties, which make them suitable for application under thermal conditions. At a high temperature, BioRoot RCS did not exhibit changes in its chemical composition. However, its film thickness was increased, and pH and solubility were reduced. Therefore, caution is needed when it is applied at high temperatures, such as during the warm obturation technique.