César Elosúa

In this study, a sol-gel film based on lead sulfide (PbS) quantum dots incorporated into a host network was synthesized as a special nanostructured composite material with potential applications in temperature sensor systems. This work dealt with the optical, structural, and morphological properties of a representative PbS quantum dot (QD)-containing thin film belonging to the Al2O3–SiO2–P2O5 system. The film was prepared using the sol-gel method combined with the spin coating technique, starting from a precursor solution containing a suspension of PbS QDs in toluene with a narrow size distribution and coated on a glass substrate in a multilayer process, followed by annealing of each deposited layer. The size (approximately 10 nm) of the lead sulfide nanocrystallites was validated by XRD and by the quantum confinement effect based on the band gap value and by TEM results. The photoluminescence peak of 1505 nm was very close to that of the precursor PbS QD solution, which demonstrated that the synthesis route of the film preserved the optical emission characteristic of the PbS QDs. The photoluminescence of the lead sulfide QD-containing film in the near infrared domain demonstrates that this material is a promising candidate for future sensing applications in temperature monitoring.