This study aims to establish a correlation between the fragmentation process and the growth mechanisms of a coating deposited on a fluoropolymer. Deposition was carried out using dielectric barrier discharge at atmospheric pressure, employing an oxygen-containing organic precursor in a nitrogen environment. The findings reveal that the impact of precursor concentration on the formation of specific functionalities is more significant than the influence of treatment time. The X-ray photoelectron spectroscopy (XPS) results obtained indicate a reduction in the N/O ratio on the coating’s surface as the precursor concentration in the discharge increases. Fourier transform infrared spectroscopy (FTIR) analysis, conducted in the spectral range of 1500 cm−1 to 1800 cm−1, confirmed the connection between the chemical properties of plasma-deposited thin films and the concentration of organic precursors in the discharge. Furthermore, the emergence of nitrile moieties (C≡N) in the FTIR spectrum at 2160 cm−1 was noted under specific experimental conditions.