Gerardo Morell

This article reports the superparamagnetic behavior of metal-free nitrogen-doped graphene quantum dots (N-GQDs). The pulsed laser ablation (PLA) method was utilized to synthesize N-GQDs with an average diameter of 3.45 nm and a high doping level (N/C) of 1.4. Magnetic properties of as-synthesized N-GQDs were explored by performing magnetization vs magnetic field (M–H) and magnetization vs temperature (M–T) measurements. M–H plots measured in a temperature range of 2–300 K revealed the superparamagnetic behavior of N-GQDs. The value of saturation magnetization was found to be directly correlated to nitrogen concentration and a saturation magnetization up to 28.7 emu/g was obtained at room temperature (300 K). M–T measurements with zero-field-cooled (ZFC) and field-cooled (FC) conditions were employed to study anisotropy energy barriers and blocking temperature. A variation in the blocking temperature (TB) from 288 to 61 K was observed when the external magnetic field (H) was changed from 0.1 to 0.6 T. The origin of superparamagnetism was attributed to the presence of graphitic nitrogen bonding configuration and defect states. The observed superparamagnetic properties along with the optical properties of N-GQDs create an opportunity for developing materials for biomedical applications and data recording devices.

In this study, we are reporting the impact of the incorporation of ferroelectric nanoparticles (FNPs), such as BaTiO3 (BTO), BiFeO3 (BFO), Bi4NdTi3Fe0.7Ni0.3O15 (BNTFN), and Bi4NdTi3Fe0.5Co0.5O15 (BNTFC), as well as the mass loading of sulfur to fabricated solvent-free sulfur/holey graphene-carbon black/polyvinylidene fluoride (S/FNPs/CBhG/PVDF) composite electrodes to achieve high areal capacity for lithium-sulfur (Li-S) batteries. The dry-press method was adopted to fabricate composite cathodes. The hG, a conductive and lightweight scaffold derived from graphene, served as a matrix to host sulfur and FNPs for the fabrication of solvent-free composites. Raman spectra confirmed the dominant hG framework for all the composites, with strong D, G, and 2D bands. The surface morphology of the fabricated cathode system showed a homogeneous distribution of FNPs throughout the composites, confirmed by the EDAX spectra. The observed Li+ ion diffusion coefficient for the composite cathode started at 2.17 × 10−16 cm2/s (S25(CBhG)65PVDF10) and reached up to the highest value (4.15 × 10−15 cm2/s) for S25BNTFC5(CBhG)60PVDF10. The best discharge capacity values for the S25(CBhG)65PVDF10 and S25BNTFC5(CBhG)60PVDF10 composites started at 1123 mAh/gs and 1509 mAh/gs and dropped to 612 mAh/gs and 572 mAh/gs, respectively, after 100 cycles; similar behavior was exhibited by the other composites that were among the best. These are better values than those previously reported in the literature. The incorporation of ferroelectric nanoparticles in the cathodes of Li-S batteries reduced the rapid formation of polysulfides due to their internal electric fields. The areal capacity for the S25(CBhG)65PVDF10 composites was 4.84 mAh/cm2 with a mass loading of 4.31 mgs/cm2, while that for the S25BNTFC5(CBhG)60PVDF10 composites was 6.74 mAh/cm2 with a mass loading of 4.46 mgs/cm2. It was confirmed that effective FNP incorporation within the S cathode improves the cycling response and stability of cathodes, enabling the high performance of Li-S batteries.