Ivana Miletić

The aim of this study was to compare the mechanical properties and ion release from a commercially available resin-modified glass ionomer cement to a formulation reinforced by the addition of short glass fibres at various percentages. Methods: Three experimental groups were prepared by adding a mass ratio of 10%, 15% and 20% of short glass fibres to the powder portion of the cement from a capsule (GC Fuji II LC), while the control group contained no fibres. Microhardness (n = 12), fracture toughness, and flexural, compressive and diametral tensile strength (n = 8) were evaluated. To study ion release, readings were obtained utilising fluoro-selective and calcium-selective electrodes after 24 h, 7 days and 30 days (n = 12). The spatial distribution of fibres within the material was evaluated through scanning electron microscopy. The data were analysed using one-way ANOVA with a Bonferroni adjustment. Results: The findings suggest that elevating fibre weight ratios to 20 wt% results in improved mechanical properties (p < 0.05) in microhardness, flexural strength, diametral tensile strength and fracture toughness. In terms of ion release, a statistically significant difference (p < 0.001) was observed between the groups at the conclusion of 24 h and 7 days, when the fluoride release was much higher in the control group. However, after 30 days, no significant distinction among the groups was identified (p > 0.05). Regarding calcium release, no statistically significant differences were observed among the groups at any of the evaluated time points (p > 0.05). SEM showed the fibres were homogeneously incorporated into the cement in all experimental groups. Conclusions: Resin-modified glass ionomer enhanced with short glass fibres at a weight loading of 20% showcased the most favourable mechanical properties while concurrently maintaining the ability to release fluoride and calcium after a 30-day period.

Over the past few decades, adhesive dentistry has advanced significantly. In light of minimal-invasive dentistry, this novel technique advocates a more conservative cavity design that relies on the efficiency of present enamel-dentine adhesives. The study aimed to address the scientific deficit in understanding the long-term bonding performance of universal adhesives and to provide a new clinical solution with desirable bond strength to dentin. The dentin bond strength of three bonding agents, G2-Bond Universal (GC), Clearfil SE Bond (Kuraray), and Scotchbond Universal Plus (3M ESPE), was evaluated following various storage and etching modes. The UltraTester (Ultradent) bond strength testing machine was used to assess shear bond strength. The results showed that thermal cycling and the choice of adhesive system significantly affected the shear bond strength (p = 0.018 and p = 0.001, respectively). Among the three adhesives, Scotchbond Universal Plus had the lowest bond strength value (mean value = 24.78 MPa), while G2-Bond Universal was found to have desirable shear bond strength to dentin compared to the other adhesives, even after one year in the oral environment (mean value = 35.15 MPa). These findings imply that the HEMA-free universal adhesive G2-Bond Universal is the most effective universal adhesive for clinical practices, particularly when applied in the self-etch mode.