Jorge de Brito

This research focuses on the utilization of recently investigated aluminosilicate industrial wastes as precursors to produce non-structural precast alkali-activated concrete pavement blocks. For this purpose, conventional blocks (200 mm × 100 mm × 80 mm) were produced using electric arc furnace slag and municipal solid waste incineration bottom ashes as the sole binders. Portland cement and fly ash blocks were produced as references. The blocks underwent a curing regimen comprising thermal, dry, and carbonation curing stages. Control uncarbonated specimens were subjected to dry curing instead of CO2-based curing to evaluate the influence of carbonation on the blocks’ strength development. The specimens were subsequently examined following EN 1338, which is the European standard for assessing and ensuring the conformity of conventional concrete pavement blocks. The carbonated blocks revealed improved mechanical and physical properties in relation to the uncarbonated ones. All blocks met standard dimensions, showed minimal skid potential (most indicating extremely low potential for slip for reporting unpolished slip resistance values exceeding 75), and had enhanced abrasion resistance due to carbonation, showing 30% and 11% less volume loss due to abrasion for fly ash and bottom ash, respectively. Carbonated blocks performed better than non-carbonated ones, displaying lower water absorption (0.58% and 0.23% less water absorption for bottom ash and slag, respectively) and higher thermal conductivity (20%, 13%, and 8% increase in values for fly ash, slag, and bottom ash, respectively). These results confirm the effectiveness of the accelerated carbonation curing technique in improving the block’s performance. Despite the promising outcomes, further optimization of the alkaline solution and carbonation curing conditions is recommended for future research.

This paper presents a literature review on the effects of accelerated carbonation on alkali-activated materials. It attempts to provide a greater understanding of the influence of CO2 curing on the chemical and physical properties of various types of alkali-activated binders used in pastes, mortars, and concrete. Several aspects related to changes in chemistry and mineralogy have been carefully identified and discussed, including depth of CO2 interaction, sequestration, reactions with calcium-based phases (e.g., calcium hydroxide and calcium silicate hydrates and calcium aluminosilicate hydrates), as well as other aspects related to the chemical composition of alkali-activated materials. Emphasis has also been given to physical alterations such as volumetric changes, density, porosity, and other microstructural properties caused by induced carbonation. Moreover, this paper reviews the influence of the accelerated carbonation curing method on the strength development of alkali-activated materials, which has been awarded little attention considering its potential. This curing technique was found to contribute to the strength development mainly through decalcification of the Ca phases existing in the alkali-activated precursor, leading to the formation of CaCO3, which leads to microstructural densification. Interestingly, this curing method seems to have much to offer in terms of mechanical performance, making it an attractive curing solution that can compensate for the loss in performance caused by less efficient alkali-activated binders replacing Portland cement. Optimising the application of such CO2-based curing methods for each of the potential alkali-activated binders is recommended for future studies for maximum microstructural improvement, and thus mechanical enhancement, to make some of the “low-performing binders” adequate Portland cement substitutes.

Climate change could have a significant impact on buildings if its effects are not properly recognized. The consequences of climate action should be considered at the design and maintenance planning stage, with the objective of promoting the overall durability of constructions. Portugal, being part of the Mediterranean region, Southern Europe, and the Iberian Peninsula, and sometimes highlighted in projections as a critical area, is an example of a country considerably vulnerable to climate change impacts. The climate is expected to become warmer and drier, with a substantial rise in temperature and fall in precipitation by the end of the century. What implications will these changes have on the degradation of façades? Climate agents, such as temperature, solar radiation, humidity, precipitation, and wind, directly influence the performance of external claddings that protect internal building components. Cement render is the prevalent façade cladding in Portugal and Europe. Research to assess the risks of future climate-induced degradation on rendered façades is relevant in the context of buildings’ durability and adaptation to climate change. The objective of the present research was to define expectations about the impact of a progressively warmer and drier climate on the degradation of exterior cement renders, based on an analysis of related literature. Generally, less staining and more cracking are expected. Expectations about salt weathering and loss of adhesion are more uncertain and need further research.