Joselito Labis

Herein, Fe3O4 core-TiO2/mesoSiO2 and Fe3O4 core-mesoSiO2/TiO2 double shell nanoparticles were prepared by first (R1) and second (R2) routes and applied for the removal of methylene blue. The reported adsorption capacities for R1-0.2, R1-0.4 and R2 samples were 128, 118 and 133 mg.g−1, respectively, which were obtained after 80 min as equilibrium contact time, and pH of 6 using a methylene blue concentration of 200 ppm. The adsorption of methylene blue using the prepared Fe3O4 core-meso SiO2/TiO2 double shell was analyzed by kinetic and isotherms models. In addition, thermodynamic investigations were applied to assess the spontaneous nature of the process. The obtained results confirmed that the pseudo-second order model is well fitted with the adsorption data and the Freundlich-isotherm assumption suggested a multilayer adsorption mechanism. In addition, results of the thermodynamic investigation indicated that ΔG° was in the range of −2.3 to −6.8 kJ/mol for R1-0.2, −2.8 to −6.3 kJ/mol for R1-0.4 and −2.0 to −5.2 kJ/mol for R2. In addition, the ΔH° and ΔS° values were found in the range of 26.4 to 36.19 kJ.mol−1 and 94.9 to 126.3 Jmol−1 K−1, respectively. These results confirm that the surfaces of Fe3O4 core-mesoSiO2/TiO2 and Fe3O4 core-TiO2/mesoSiO2 double shell exhibit a spontaneous tendency to adsorb methylene blue from the aqueous solutions. The achieved performance of Fe3O4 core-meso SiO2/TiO2 and Fe3O4 core-TiO2/meso SiO2 double shell as adsorbent for methylene blue removal will encourage future research investigations on the removal of a broad range of contaminants from wastewater.

In this paper, a unique hybrid approach to design and synthesize 2D/3D Al2O3-ZnO nanostructures by simultaneous deposition is presented. Pulsed laser deposition (PLD) and RF magnetron sputtering (RFMS) methods are redeveloped into a single tandem system to create a mixed-species plasma to grow ZnO nanostructures for gas sensing applications. In this set-up, the parameters of PLD have been optimized and explored with RFMS parameters to design 2D/3D Al2O3-ZnO nanostructures, including nanoneedles/nanospikes, nanowalls, and nanorods, among others. The RF power of magnetron system with Al2O3 target is explored from 10 to 50 W, while the ZnO-loaded PLD’s laser fluence and background gases are optimized to simultaneously grow ZnO and Al2O3-ZnO nanostructures. The nanostructures are either grown via 2-step template approach, or by direct growth on Si (111) and MgO<0001> substrates. In this approach, a thin ZnO template/film was initially grown on the substrate by PLD at ~300 °C under ~10 milliTorr (1.3 Pa) O2 background pressure, followed by growth of either ZnO or Al2O3-ZnO, using PLD and RFMS simultaneously under 0.1–0.5 Torr (13–67 Pa), and Ar or Ar/O2 background in the substrate temperate range of 550–700 °C. Growth mechanisms are then proposed to explain the formation of Al2O3-ZnO nanostructures. The optimized parameters from PLD-RFMS are then used to grow nanostructures on Au-patterned Al2O3-based gas sensor to test its response to CO gas from 200 to 400 °C, and a good response is observed at ~350 °C. The grown ZnO and Al2O3-ZnO nanostructures are quite exceptional and remarkable and have potential applications in optoelectronics, such in bio/gas sensors.