Hierarchical porous carbon materials have received significant attention for application in catalytic water splitting because of their high efficiency, cost-effectiveness, and biocompatibility. In this study, laser-induced graphene (LIG) was fabricated on a carbon film- (CF-) type substrate for an efficient hydrogen evolution reaction (HER). The LIG-CF electrode was fabricated via laser-induced graphitization on a commercial polyimide (PI) film, followed by the pyrolysis of the LIG on the PI film (LIG-PI). During pyrolysis, the microscopic and material properties of the LIG remained intact, as verified through various characterizations. The as-prepared all-carbon electrode was then utilized as an electrode for the HER study in a 1.0 M KOH electrolyte and compared with LIG-PI and Pt electrodes. In the HER experiments, the optimized LIG-CF electrode exhibited excellent catalytic performance with zero-onset potential, and the potentials required to achieve high current densities of 10 and 20 mA/cm2 were 134 and 139 mV (vs. reversible hydrogen electrode (RHE)), respectively. The excellent performance of the LIG-CF electrode originates from the hierarchical porous structure of the LIG material, which serves as an electrochemically active site, and carbon substrate that facilitates the fast transport of ions at the electrode/electrolyte interface. Additionally, the carbon substrate shortens the transportation length of electrons which played a significant role for the enhanced performance of the LIG-CF electrode.

This study describes the single-step synthesis of a mesoporous layered nickel-chromium-sulfide (NCS) and its hybridization with single-layered graphene oxide (GO) using a facile, inexpensive chemical method. The conductive GO plays a critical role in improving the physicochemical and electrochemical properties of hybridized NCS/reduced GO (NCSG) materials. The optimized mesoporous nanohybrid NCSG is obtained when hybridized with 20% GO, and this material exhibits a very high specific surface area of 685.84 m2/g compared to 149.37 m2/g for bare NCS, and the pore diameters are 15.81 and 13.85 nm, respectively. The three-fold superior specific capacity of this optimal NCSG (1932 C/g) is demonstrated over NCS (676 C/g) at a current density of 2 A/g. A fabricated hybrid supercapacitor (HSC) reveals a maximum specific capacity of 224 C/g at a 5 A/g current density. The HSC reached an outstanding energy density of 105 Wh/kg with a maximum power density of 11,250 W/kg. A 4% decrement was observed during the cyclic stability study of the HSC over 5000 successive charge–discharge cycles at a 10 A/g current density. These results suggest that the prepared nanohybrid NCSG is an excellent cathode material for gaining a high energy density in an HSC.