Pure Ce0.5Zr0.5O2 and Au (0.1–1.0 wt.%)-deposited Ce0.5Zr0.5O2 nanomaterials were synthesized via hydrothermal and non-aqueous precipitation methods using gold acetate as a chloride-free Au precursor. The synthesized nanostructures exhibited enhanced photocatalytic activity for hydrogen production via aqueous bioethanol photoreforming under visible light. Different characterization tools such as powder XRD, HRTEM, FT-IR, DR UV-vis, XPS and N2 gas adsorption were used to analyze the physicochemical properties of the synthesized photocatalysts. The band gap value was lowered from 3.25 eV to 2.86 eV after Au nanoparticles were deposited on the surface of Ce0.5Zr0.5O2. The 1.0 wt.% Au-deposited Ce0.5Zr0.5O2 sample exhibited the highest photocatalytic activity for H2 production (3210 μmol g−1) due to its low band gap, the presence of more oxygen vacancies and its porous character. The EIS results reveal that the deposition of 1.0 wt.% Au nanoparticles is responsible for the highest charge separation efficiency with an increased lifetime of photogenerated e−/h+ species compared to the other samples. In addition, the presence of plasmonic Au is responsible for the effectiveness of the electron trap in improving the rate of H2 formation.

Biodiesel has been recognized as an environmentally friendly, renewable alternative to fossil fuels. In this work, CaO/ZnCo2O4 nanocomposites were successfully synthesized via simple mechanochemical reaction between ZnCo2O4 and CaO powders by varying the CaO loading from 5 to 20 wt.%. The synthesized materials were found to be highly efficient heterogeneous catalysts for transesterification of tributyrin with methanol to produce biodiesel. The nanocomposite, which contained 20 wt.% CaO and 80 wt.% ZnCo2O4 (CaO/ZnCo2O4-20), exhibited superior and stable transesterification activity (98% conversion) under optimized reaction conditions (1:12 TBT to methanol molar ratio, 5 wt.% catalyst and 180 min. reaction time). The experimental results revealed that the reaction mechanism on the CaO/ZnCo2O4 composite followed pseudo first-order kinetics. The physicochemical characteristics of the synthesized nanocomposites were measured using X-ray diffraction (XRD), high resolution transmission electron microscopy (HRTEM), Fourier-transformed infrared spectroscopy (FTIR), X-ray photoelectron spectrometer (XPS), N2-physisorption, and CO2- temperature-programmed desorption (CO2-TPD) techniques. The results indicated the existence of coalescence between the CaO and ZnCo2O4 particles, Additionally, the CaO/ZnCo2O4-20 catalyst was found to possess the greater number of highly basic sites and high porosity, which are the key factors affecting catalytic performance in transesterification reactions.