This study focuses on epoxy hybrid systems prepared by incorporating multi-wall carbon nanotubes (MWCNTs) and graphene nanosheets (GNs) at two fixed filler amounts: below (0.1 wt%) and above (0.5 wt%), with varying MWCNT:GN mix ratios. The hybrid epoxy systems exhibited remarkable electrical performance, attributed to the π–π bond interactions between the multi-wall carbon nanotubes and the graphene layers dispersed in the epoxy resin matrix. The material’s properties were characterized through dynamic mechanical and thermal analyses over a wide range of temperatures. In addition to excellent electrical properties, the formulated hybrid systems demonstrated high mechanical performance and thermal stability. Notably, the glass transition temperature of the samples reached 255 °C, and high storage modulus values at elevated temperatures were observed. The hybrid systems also displayed thermal stability up to 360 °C in air. By comparing the mechanical and electrical performance, the formulation can be optimized in terms of the electrical percolation threshold (EPT), electrical conductivity, thermostability, and mechanical parameters. This research provides valuable insights for designing advanced epoxy-based materials with multifunctional properties.

This work deals with developing a self-healing resin designed for aeronautical and aerospace applications. The bifunctional epoxy precursor was suitably functionalized to enhance its toughness to realize good compatibilization with a rubber phase dispersed in the hosting epoxy resin. Subsequently, the resulting mixture was loaded with healing molecules. The effect of the temperature on the epoxy precursor’s functionalization process was deeply studied. Fourier trans-former infrared (FT-IR) spectroscopy and dynamic mechanical analyses (DMA) evidenced that the highest temperature (160 °C) allows for obtaining a bigger amount of rubber phase bonded to the matrix. Elastomeric domains of dimensions lower than 500–600 nanometers were found well distributed in the matrix. Self-healing efficiency evaluated with the tapered double cantilever beam (TDCB) method evidenced a healing efficiency for the system functionalized at 160 °C higher than 69% for all the explored fillers. The highest value was detected for the sample with DBA, for which 88% was found. The healing efficiency of the same sample functionalized at 120 °C was found to decrease to the value of 52%. These results evidence the relevant role of the amount and distribution of rubber domains into the resin for improving the resin’s dynamic properties. The adopted strategy allows for optimizing the self-healing performance.