Lisa Ernst

In the healthcare system, lower leg fractures remain relevant, incurring costs related to surgical treatment, hospitalization, and rehabilitation. The duration of treatment may vary depending on the individual case and its severity. Casting as a post-surgical fracture treatment is a common method in human and experimental veterinary medicine. Despite the high importance of sheep in preclinical testing materials for osteosynthesis, there is no standardised cast system ensuring proper stabilisation and functionality of hind limbs during the healing of tibia fractures or defects. Existing treatment approaches for tibial osteosynthesis in laboratory animal science include sling hanging, external fixators, or former Achilles tendon incision. These methods restrict animal movement for 4–6 weeks, limit species-typical behaviour, and impact social interactions. Our pilot study introduces a Standardised Walking Cast (SWC) for sheep, enabling immediate physiological movement post surgery. Seven Rhone sheep (female, 63.5 kg ± 6.45 kg) each with a single tibia defect (6 mm mechanical drilled defect) underwent SWC application for 4 weeks after plate osteosynthesis. The animals bore weight on their operated leg from day one, exhibiting slight lameness (grade 1–2 out of 5). Individual step lengths showed good uniformity (average deviation: 0.89 cm). Group housing successfully started on day three after surgery. Weekly X-rays and cast changes ensured proper placement, depicting the healing process. This study demonstrates the feasibility of using an SWC for up to 72 kg of body weight without sling hanging via ceiling mounting or external fixation techniques. Allowing species-typical movement and social behaviour can significantly improve the physiological behaviour of sheep in experiments, contributing to refinement.

Tissue adhesives constitute a great possibility to improve conventional wound closure. In contrast to sutures, they enable nearly immediate hemostasis and can prevent fluid or air leaks. In the present study, a poly(ester)urethane-based adhesive was investigated which already proved to be suitable for different indications, such as reinforcing vascular anastomosis and sealing liver tissue. Using in vitro and in vivo setups, the degradation of the adhesives was monitored over a period of up to 2 years, to evaluate long-term biocompatibility and determine degradation kinetics. For the first time, the complete degradation of the adhesive was documented. In subcutaneous locations, tissue residues were found after 12 months and in intramuscular locations, tissue degradation was complete after about 6 months. A detailed histological evaluation of the local tissue reaction revealed good biocompatibility throughout the different degradation stages. After full degradation, complete remodeling to physiological tissue was observed at the implant locations. In addition, this study critically discusses common issues related to the assessment of biomaterial degradation kinetics in the context of medical device certification. This work highlighted the importance and encouraged the implementation of biologically relevant in vitro degradation models to replace animal studies or at least reduce the number of animals in preclinical testing prior to clinical studies. Moreover, the suitability of frequently used implantation studies based on ISO 10993-6 at standard locations was critically discussed, especially in light of the associated lack of reliable predictions for degradation kinetics at the clinically relevant site of implantation.