This research presents a novel approach to synthesising polyurethane (PUR)-based aerogels at the pilot scale, optimizing synthesis variables such as the gelation solvent, solids content, chain extender/isocyanate ratio, and dispersion mode. The solids content (2–11 wt.%) is the parameter with the most influence on the density of the aerogels, with a clear decrease in this property as the solids content decreases. On the other hand, it was demonstrated that minimizing the excess of ethylenediamine (used as chain extender) in relation to the isocyanate is a valuable consideration to improve the thermal conductivity of the aerogel. Related to the chain extender/isocyanate ratio, a compromise situation where the initial isocyanate reacts almost completely is crucial. Fourier-transform infrared spectroscopy was used to conduct such monitoring during the reaction. Once the conditions were optimised, the aerogel showing improved properties was synthesised using ethyl acetate as the gelling solvent, a 3.7 wt.% solids content, an ethylenediamine/isocyanate ratio of 0.20, and sonication as the dispersion mode, attaining a thermal conductivity of 0.030 W m−1 K−1 and a density of 0.046 g cm−3. Therefore, the synthesized aerogel emerges as a promising candidate for use in the construction and automotive industries.