Nagih M. Shaalan

This work comprehensively studies both the photocatalytic degradation and the adsorption process of Congo red dye on the surface of a mixed-phase copper oxide–graphene heterostructure nanocomposite. Laser-induced pristine graphene and graphene doped with different CuO concentrations were used to study these effects. Raman spectra showed a shift in the D and G bands of the graphene due to incorporating copper phases into the laser-induced graphene. The XRD confirmed that the laser beam was able to reduce the CuO phase to Cu2O and Cu phases, which were embedded into the graphene. The results elucidate incorporating Cu2O molecules and atoms into the graphene lattice. The production of disordered graphene and the mixed phases of oxides and graphene were validated by the Raman spectra. It is noted from the spectra that the D site changed significantly after the addition of doping, which indicates the incorporation of Cu2O in the graphene. The impact of the graphene content was examined with 0.5, 1.0, and 2.0 mL of CuO. The findings of the photocatalysis and adsorption studies showed an improvement in the heterojunction of copper oxide and graphene, but a significant improvement was noticed with the addition of graphene with CuO. The outcomes demonstrated the compound’s potential for photocatalytic use in the degradation of Congo red.

In this work, the deposition of titanium nitride (TiN) thin film using direct current (DC) sputtering technique and its application as diffusion barriers against copper interconnect was presented. The deposited film was analyzed by using X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), and X-ray photoelectron spectroscopy (XPS) techniques. XRD patterns showed the face-centered cubic (FCC) structure for the TiN/SiO2/Si film, having (111) and (200) peaks and TiN (111), Cu(111), and Cu(200) peaks for Cu/TiN/SiO2/Si film. FESEM images revealed that the grains were homogeneously dispersed on the surface of the TiN film, having a finite size. XPS study showed that Ti2p doublet with peaks centered at 455.1 eV and 461.0 eV for TiN film was observed. Furthermore, the stoichiometry of the deposited TiN film was found to be 0.98. The sheet resistance of the TiN film was analyzed by using a four-point probe method, and the resistivity was calculated to be 11 μΩ cm. For the utilization, TiN film were tested for diffusion barrier performance against Cu interconnect. The results exhibited that TiN film has excellent performance in diffusion barrier for copper metallization up to a temperature of 700 °C. However, at a higher annealing temperature of 800 °C, the formation of Cu3Si and TiSi2 compounds were evident. Thus, stoichiometric TiN film with high thermal stability and low resistivity produced in this study could be applied for the fabrication of microelectronic devices.

In this study, the enhanced photodegradation of a high-concentration phenol red (PR) using very fine TiO2 nanocrystals by adding a KBrO3 electron acceptor was reported for the first time. The structural study on TiO2 nanocrystals using HRTEM, XRD, Raman, and EDX was performed and it confirmed the anatase phase of TiO2 nanocrystals. UV–Vis absorbance of 20 mg.L−1 PR was measured and the photodegradation was extracted. The KBrO3 concentration effects exhibited an important enhancement in the degradation of PR dye. The efficiency of PR was increased during 110 min from 75% of pure TiO2 to 92% and 98% of TiO2 with 1 mg and 5 mg KBrO3, respectively. For different samples, a first-order kinetic of dye degradation is confirmed. The instantaneous amount of degraded dye increased from 150 to 180 and 197 mg/g TiO2 with 1 mg and 5 mg KBrO3, respectively. The mechanism of the photodegradation reaction confirms the effect of OH- radicals on increasing the photocatalytic activities. The addition of electron acceptors KBrO3 improved the photocatalysis rate, where it prevented e-h recombination through conduction band electron capture, which increases the concentration of hydroxyl radicals. The proposed mechanism and results were supported by photocurrent measurements and a Raman spectra analysis of the final photodegraded products. The photocurrent of TiO2 was observed at 1.2 µA, which was significantly improved up to 13.2, and 21.3 µA with the addition of 1 mg and 5 mg of KBrO3. The Raman spectra of the final products confirmed that SO42− and carbons are byproducts of PR degradation.