Natalia P. Klochko

In this work, to obtain textile triboelectric layers for wearable flexible triboelectric nanogenerators (TENGs), we used two modes of growing nanostructured zinc oxide (ZnO) arrays on a carbon fabric (CF) using the automatic Successive Ionic Layer Adsorption and Reaction (SILAR) method. To produce a CF/ZnO_nr triboelectric textile with an array of intergrown short ZnO nanorods, we used a pre-coating of carbon fibers with ZnO seed layers. When the ZnO layer was fabricated by automatic SILAR on bare carbon fabric, we obtained the CF/ZnO_ns textile with an array of interconnected ZnO nanosheets 50–100 nm thick. As a proof of concept, we developed and tested two prototypes of flexible vertical contact–separation mode CF/ZnO_nr/PET/ITO and CF/ZnO_ns/PET/ITO TENGs, in which a gap was involuntarily formed between the smooth PET layer and the woven carbon textile coated with nanostructured ZnO films. In pressing tests with a force of ~5 N (pressure ~33 kPa), the CF/ZnO_ns/PET/ITO TENG created a higher open-circuit voltage up to 30 V and a higher maximum surface charge density of 1.3 μC/m2. In the successive press–release tests, this TENG showed an output voltage of 3.6 V, a current density of 1.47 μA/cm2, and a power density of 1.8 µW/cm2, confirming its effectiveness.