Paolo Pesce

Background: Fiber-reinforced composites (FRCs) have been proposed as an alternative to traditional metal alloys for the realization of frameworks in full-arch implant-supported prostheses. The aim of the present in vitro study was to evaluate the deflection under load of seven prostheses endowed with frameworks made of different materials, including different types of fiber-reinforced composites (FRCs). Methods: A master cast with four implant analogues in correspondence with the two lateral incisors and the two first molars was used to create full-arch fixed prostheses with the same shape and different materials. Prostheses were made of the following different materials (framework+veneering material): gold alloy+resin (Au+R), titanium+resin (Ti+R), FRC with multidirectional carbon fibers+resin (ICFRC+AR), FRC with unidirectional carbon fibers+composite (UCFRC+C), FRC with glass fibers+resin (GFRC+AR), FRC with glass fibers+composite (GFRC+C), and resin (R, fully acrylic prosthesis). Flexural tests were conducted using a Zwick/Roell Z 0.5 machine, and the deflection of the lower surface of the prosthesis was measured in order to obtain load/deflection graphs. Results: Greater rigidity and less deflection were recorded for UCFRC+C and GFRC+C, followed by Ti+R and Au+R. The greatest deformations were observed for resin alone, ICFRC+R, and GFRC+R. The results were slightly different in the incisal region, probably due to the greater amount of veneering material in this area. Conclusions: When used to realize full-arch frameworks, Au and Ti allow for predictable mechanical behavior with gradual deformations with increasing load. UCFRC also demonstrated good outcomes and less deflection than ICFRCs when loaded. The GFRC full-arch framework may be a valid alternative, although it showed greater deflections. Further studies are needed in order to evaluate how different prosthesis designs and material thicknesses might affect the outcomes.

Background: Restorative materials might significantly affect load transmission in peri-implant bone. The aim of the present study is to evaluate the shock absorption capacity of two different polymeric materials to be used for implant-supported prostheses. Methods: A masticatory robot was used to compare the shock absorption capacity of veneered and non-veneered polyetherketoneketone (PEKK), Pekkton®ivory (Cendres+Mètaux), and the glass fiber-reinforced composite (GFRC), TRINIATM (Bicon). Five identical sample crowns for each of the three groups were tested. Forces transmitted at the simulated peri-implant bone were recorded and statistically analyzed. Results: The statistical analysis of forces transmitted at the simulated dental implant revealed significant differences between the materials tested and between these materials and zirconia, glass ceramic, composite resin, and acrylic resin. Only differences between PEKK and veneered PEKK and between PEKK and one of the previously tested composite resins were not statistically significant. PEKK samples demonstrated significantly greater shock absorption capacity compared to GFRC. Conclusions: PEKK revealed optimal shock absorption capacity. Further studies are needed to evaluate its efficacy in the case of long-span prostheses with reduced prosthetic volume.