In this study, gelatin-based films containing graphene nanoparticles were obtained. Nanoparticles were taken from four chosen commercial graphene nanoplatelets with different surface areas, such as 150 m2/g, 300 m2/g, 500 m2/g, and 750 m2/g, obtained in different conditions. Their morphology was observed using SEM with STEM mode; porosity, Raman spectra and elemental analysis were checked; and biological properties, such as hemolysis and cytotoxicity, were evaluated. Then, the selected biocompatible nanoparticles were used as the gelatin film modification with 10% concentration. As a result of solvent evaporation, homogeneous thin films were obtained. The surface’s properties, mechanical strength, antioxidant activity, and water vapor permeation rate were examined to select the appropriate film for biomedical applications. We found that the addition of graphene nanoplatelets had a significant effect on the properties of materials, improving surface roughness, surface free energy, antioxidant activity, tensile strength, and Young’s modulus. For the most favorable candidate for wound dressing applications, we chose a gelatin film containing nanoparticles with a surface area of 500 m2/g.

For the first time, organic light-emitting diodes (OLEDs) based on bis(8-hydroxyquinoline) zinc with a styryl group (ZnStq) dispersed in poly(N-vinylcarbazole) matrix (ZnStq_R:PVK, where R = H, Cl, OCH3) were fabricated. The ZnStq_R:PVK films made via the spin-coating method were used as the active layer in these devices. The produced OLEDs showed strong electroluminescence with yellow emissions at 590, 587 and 578 nm for the ZnStq_H:PVK, ZnStq_Cl:PVK and ZnStq_OCH3:PVK, respectively. For all the studied thin films, the main photoluminescence emission bands were observed between 565 and 571 nm. The OLED with the ZnStq_OCH3:PVK layer with a narrow electroluminescence spectrum was found to have sufficient color purity to produce ultra-high-resolution displays with reduced power consumption (full width at half maximum of 59 nm, maximum brightness of 2244 cd/m2 and maximum current efficiency of 1.24 cd/A, with a turn-on voltage of 6.94 V and a threshold voltage of 7.35 V). To characterize the photophysical properties of the active layer, the ZnStq_R:PVK layers samples were additionally deposited on glass and silicon substrates. We found that the obtained results predestine ZnStq_R:PVK layers for use in the lighting industry in the future.