Salete S. Balula

The composites of heteropolyacids (H3PW12, H3PMo12) incorporated into amine-functionalized silica materials were used for the first time as heterogeneous catalysts in the valorization of glycerol (a major waste from the biodiesel industry) through acetalization reaction with acetone. The polyoxotungstate catalyst H3PW12@AptesSBA-15 exhibited higher catalytic efficiency than the phosphomolybdate, achieving 97% conversion and 97% of solketal selectivity, after 60 min at 25 °C, or 91% glycerol conversion and the same selectivity, after 5 min, performing the reaction at 60 °C. A correlation between catalytic performance and catalyst acidity is presented here. Furthermore, the stability of the solid catalyst was investigated and discussed.

The adsorptive performance of mesoporous silica-based materials towards inorganic (metal ions) and organic (dyes) water pollutants was investigated. Mesoporous silica materials with different particle size, surface area and pore volume were prepared and tailored with different functional groups. These materials were then characterised by solid-state techniques, namely vibrational spectroscopy, elemental analysis, scanning electron microscopy and nitrogen adsorption–desorption isotherms, allowing the successful preparation and structural modifications of the materials to be confirmed. The influence of the physicochemical properties of the adsorbents towards the removal of metal ions (Ni2+, Cu2+ and Fe3+) and organic dyes (methylene blue and methyl green) from aqueous solutions was also investigated. The results reveal that the exceptionally high surface area and suitable ζ-potential of the nanosized mesoporous silica nanoparticles (MSNPs) seem to favour the adsorptive capacity of the material for both types of water pollutants. Kinetic studies were performed for the adsorption of organic dyes by MSNPs and large-pore mesoporous silica (LPMS), suggesting that the process follows a pseudo-second-order model. The recyclability along consecutive adsorption cycles and the stability of the adsorbents after use were also investigated, showing that the material can be reused. Current results show the potentialities of novel silica-based material as a suitable adsorbent to remove pollutants from aquatic matrices with an applicability to reduce water pollution.

A successful encapsulation of Keggin-type polyoxomolybdate (H3[PMo12O40], PMo12) into metal-organic framework (MOF) materials with an identical framework but distinct metal centers (ZIF-8 with Zn2+ and ZIF-67 with Co2+) was accomplished by a straightforward room-temperature procedure. The presence of Zn2+ in the composite material PMo12@ZIF-8 instead of Co2+ in PMo12@ZIF-67 caused a remarkable increase in the catalytic activity that achieved a total oxidative desulfurization of a multicomponent model diesel under moderate and friendly conditions (oxidant: H2O2 and solvent: ionic liquid, IL). Interestingly, the parent ZIF-8-based composite with the Keggin-type polyoxotungstate (H3[PW12O40], PW12), PW12@ZIF-8, did not show the relevant catalytic activity. The ZIF-type supports present an appropriate framework to accommodate active polyoxometalates (POMs) into their cavities without leaching, but the nature of the metallic center from the POM and the metal present in the ZIF framework were vital for the catalytic performance of the composite materials.