Teemu Ovaska

This study evaluated the compatibility with steels for three B20 fuel samples blended from fossil diesel and used cooking oil methyl ester. One sample was untreated and its concentration of copper was analyzed as <1 ppm. Another sample was doped by adding Cu at a concentration of ≤2 ppm and the third sample by adding Cu at a concentration of ≤4 ppm. Steel samples (carbon steel, stainless steel and a special alloy) were then put into the fuel blends and stored at 50 °C for 692 h. After storing, the metal concentrations of the fuel blends were again analyzed, and signs of corrosion were evaluated visually. The aim of this study was to find out if the fuel already contaminated by copper will affect the corrosion of the chosen steel qualities. Additionally, fuel properties were measured for all three blend samples before the immersion of steels. Visual evaluation of the steels indicated that signs of corrosion were seen in all studied samples, but Cu doping did not increase the signs of corrosion notably. The results also showed that the copper content from 1 to 2 and 4 ppm reduced the oxidation stability and increased the acid number of the fuel samples.