Amanullah Fatehmulla

Photocatalytic reduction of CO2 with CH4 through the dry reforming of methane (DRM) is an attractive approach to recycling greenhouse gases into valuable chemicals and fuels; however, this process is quite challenging. Although there is growing interest in designing efficient photocatalysts, they are less stable, and have lower photoactivity when employed for DRM reactions. Herein, we developed a noble metal-free hierarchical graphitic carbon nitride (HC3N4) loaded with cobalt (Co) for highly efficient and stable photocatalytic dry reforming of methane to produce synthesis gases (CO and H2). The performance of the newly designed Co/HC3N4 composite was tested for different reforming systems such as the dry reforming of methane, bi-reforming of methane (BRM) and reforming of CO2 with methanol–water. The performance of HC3N4 was much higher compared to bulk g-C3N4, whereas Co/HC3N4 was found to be promising for higher charge carrier separation and visible light absorption. The yield of CO and H2 with HC3N4 was 1.85- and 1.81-fold higher than when using g-C3N4 due to higher charge carrier separation. The optimized 2% Co/HC3N4 produces CO and H2 at an evolution rate of 555 and 41.2 µmol g−1 h−1, which was 18.28- and 1.74-fold more than using HC3N4 during photocatalytic dry reforming of methane (DRM), with a CH4/CO2 feed ratio of 1.0. This significantly enhanced photocatalytic CO and H2 evolution during DRM was due to efficient charge carrier separation in the presence of Co. The CH4/CO2 feed ratio was further investigated, and a 2:1 ratio was best for CO production. In contrast, the highest H2 was produced with a 1:1 feed ratio due to the competitive adsorption of the reactants over the catalyst surface. The performance of the composite was further investigated for bi-reforming methane and methanol. Using photocatalytic CO2 reduction with CH4/H2O, the production of CO and H2 was reduced, whereas significantly higher CO and H2 evolved using the BRM process involving methanol. Using methanol with CO2 and H2O, 10.77- and 1.39-fold more H2 and CO efficiency was achieved than when using dry reforming of methane. The composite was also very stable for continuous synthesis gas production during DRM in consecutive cycles. Thus, a co-assisted g-C3N4 nanotexture is promising for promoting photocatalytic activity and can be further explored in other solar energy applications.

Nanoscale ZnO is a vital semiconductor material whose versatility can be enhanced by sensitizing it with metals, especially noble metals, such as gold (Au). ZnO quantum dots were prepared via a simple co-precipitation technique using 2-methoxy ethanol as the solvent and KOH as the pH regulator for hydrolysis. The synthesized ZnO quantum dots were deposited onto glass slides using a simple doctor blade technique. Subsequently, the films were decorated with gold nanoparticles of different sizes using a drop-casting method. The resultant films were characterized via various strategies to obtain structural, optical, morphological, and particle size information. The X-ray diffraction (XRD) reveals the formation of the hexagonal crystal structure of ZnO. Upon Au nanoparticles loading, peaks due to gold are also observed. The optical properties study shows a slight change in the band gap due to Au loading. Nanoscale sizes of particles have been confirmed through electron microscope studies. P.L. studies display blue and blue-green band emissions. The significant degradation efficiency of 90.2% methylene blue (M.B.) was attained in natural pH in 120 min using pure ZnO catalyst while one drop gold-loaded catalysts, ZnO: Au 5 nm, ZnO: Au 7 nm, ZnO: Au 10 nm and ZnO: Au 15 nm, delivered M.B. degradation efficiency of 74.5% (in 245 min), 63.8% (240 min), 49.6% (240 min) and 34.0% (170 min) in natural pH, respectively. Such films can be helpful in conventional catalysis, photocatalysis, gas sensing, biosensing, and photoactive applications.