The development of cost-effective technologies for the treatment of water contaminated by petrochemicals is an environmental priority. This issue is of paramount importance for countries like Saudi Arabia owing to its scarce water resources. Of particular concern are automobile fuels, such as gasoline and diesel, that can contaminate water aquifers from leaking underground fuel storage tanks. Owing to the cost-effectiveness of adsorption-based technologies, low-cost high surface-area commercial activated carbon was used for the adsorptive removal of contaminants from the emulsified fuel-contaminated water. Batch equilibrium experiments showed a high efficacy of the adsorbent. Even with small amounts of the adsorbent, a removal efficiency of more than 97% was obtained for both gasoline as well as diesel. Three different well-known batch adsorption isotherm models, namely the Langmuir, Freundlich, and Temkin, were used for describing the experimental data. The best results were obtained using the Freundlich isotherm followed by the Langmuir model. The maximum capacity was found to be 8.3 g gasoline and 9.3 g diesel per gram of the adsorbent at ambient conditions for a neutral contaminated aqueous solution.

Nanoscale ZnO is a vital semiconductor material whose versatility can be enhanced by sensitizing it with metals, especially noble metals, such as gold (Au). ZnO quantum dots were prepared via a simple co-precipitation technique using 2-methoxy ethanol as the solvent and KOH as the pH regulator for hydrolysis. The synthesized ZnO quantum dots were deposited onto glass slides using a simple doctor blade technique. Subsequently, the films were decorated with gold nanoparticles of different sizes using a drop-casting method. The resultant films were characterized via various strategies to obtain structural, optical, morphological, and particle size information. The X-ray diffraction (XRD) reveals the formation of the hexagonal crystal structure of ZnO. Upon Au nanoparticles loading, peaks due to gold are also observed. The optical properties study shows a slight change in the band gap due to Au loading. Nanoscale sizes of particles have been confirmed through electron microscope studies. P.L. studies display blue and blue-green band emissions. The significant degradation efficiency of 90.2% methylene blue (M.B.) was attained in natural pH in 120 min using pure ZnO catalyst while one drop gold-loaded catalysts, ZnO: Au 5 nm, ZnO: Au 7 nm, ZnO: Au 10 nm and ZnO: Au 15 nm, delivered M.B. degradation efficiency of 74.5% (in 245 min), 63.8% (240 min), 49.6% (240 min) and 34.0% (170 min) in natural pH, respectively. Such films can be helpful in conventional catalysis, photocatalysis, gas sensing, biosensing, and photoactive applications.