Felix Burkhardt

The aim of this in vitro study was to evaluate the long-term stability of one-piece diameter reduced zirconia oral implants under the influence of loading and artificial aging in a chewing simulator as well as the fracture load in a static loading test. Thirty-two one-piece zirconia implants with a diameter of 3.6 mm were embedded according to the ISO 14801:2016 standard. The implants were divided into four groups of eight implants. The implants of group DLHT were dynamically loaded (DL) in a chewing simulator for 107 cycles with a load of 98 N and simultaneously hydrothermally aged (HT) using a hot water bath at 85 °C. Group DL was only subjected to dynamic loading and group HT was exclusively subjected to hydrothermal aging. Group 0 acted as a control group: no dynamical loading, no hydrothermal ageing. After exposure to the chewing simulator, the implants were statically loaded to fracture in a universal testing machine. To evaluate group differences in the fracture load and bending moments, a one-way ANOVA with Bonferroni correction for multiple testing was performed. The level of significance was set to p < 0.05. In the static loading test, group DLHT showed a mean fracture load of 511 N, group DL of 569 N, group HT of 588 N and control group 0 of 516 N. The average bending moments had the following values: DLHT: 283.5 Ncm; DL: 313.7 Ncm; HT: 324.4 Ncm; 0: 284.5 Ncm. No significant differences could be found between the groups. Hydrothermal aging and/or dynamic loading had no significant effect on the stability of the one-piece diameter reduced zirconia implants (p > 0.05). Within the limits of this investigation, it can be concluded that dynamic loading, hydrothermal aging and the combination of loading and aging did not negatively influence the fracture load of the implant system. The artificial chewing results and the fracture load values indicate that the investigated implant system seems to be able to resist physiological chewing forces also over a long service period.

Objective To investigate the fracture strength and potential phase transformation of an injection‐molded two‐piece zirconia implant restored with a zirconia abutment after loading and/or aging. Methods Thirty‐two two‐piece zirconia implants (4.0 mm diameter) restored with zirconia abutments were embedded according to ISO 14801 and divided into four groups ( n = 8/group): Three groups were either exclusively hydrothermally treated (group HT; 85°C), dynamically loaded (group DL; 10 7 cycles; 98 N), or subjected to both treatments simultaneously (group DL/HT). One group remained untreated (group 0). A sample from each group was cross‐sectioned and examined by scanning electron microscopy for possible crystal phase transformation. The remaining samples were then loaded to fracture in a static loading test. A one‐way ANOVA was used for statistical analyses. Results During dynamic loading, three implants of group DL and six implants of group DL/HT fractured at a load of 98 N. The fracture strength of group DL/HT (108 ± 141 Ncm) was significantly reduced compared to the other groups (group 0: 342 ± 36 Ncm; HT: 363 ± 49 Ncm; DL: 264 ± 198 Ncm) ( p < .05). Fractures from group 0 and HT occurred at both implant and abutment level, whereas implants from group DL and DL/HT fractured only at implant level. A shallow monoclinic transformation zone of approximately 2 μm was observed following hydrothermal treatment. Conclusions Within the limitations of this study, it can be concluded that dynamic loading and the combination of loading and aging reduced the fracture strength of the implant abutment combination. Hydrothermal treatment caused a shallow transformation zone which had no influence on the fracture strength.