The use of hybrid abutment crowns bonded extraorally to a titanium bonding base has aesthetic and biological benefits for the prosthetic rehabilitation of oral implants. The objective of this study was to evaluate the effects of luting agents between a zirconium dioxide crown and the titanium bonding base on crown/abutment retention and the subsequent durability of the prosthetic superstructure. Fifty-six implant abutment samples, all restored with a lower first premolar zirconium dioxide crown, were used and divided into seven groups (n = 8/group) according to the type of luting agent used: group 1, SpeedCEM Plus; group 2, Panavia SA Cement Universal; group 3, Panavia V5; group 4, RelyX Unicem 2 Automix; group 5, VITA ADIVA IA-Cem; group 6, Ketac CEM; and group 7, Hoffmann’s Phosphate Cement. All specimens were subjected to thermomechanical loading (load of 49 N, 5 million chewing cycles and 54.825 thermocycles in water with temperatures of 5 °C and 55 °C). The surviving samples were exposed to a pull-off force until crown debonding from the bonding base. Overall, 55 samples survived the thermomechanical load. Group 2 showed the highest mean pull-off force value (762 N), whereas group 6 showed the lowest mean value (55 N). The differences between the seven groups were statistically significant (ANOVA, p < 0.001). The debonding failure pattern was mainly adhesive and was noticed predominantly at the zirconium dioxide–luting agent interface. Within the scope of the present investigation, it was shown that most of the luting agents are suitable for “cementation” of a zirconium dioxide crown onto a titanium base since the debonding forces are above a recommended value (159 N).