The paper presents the results of the analysis of the resistance to hydrogen and high-temperature salt corrosion of the developed alloy of the CM88Y type for the turbine blades of gas turbine engines for marine and power purposes in comparison with the industrial heat-resistant corrosion-resistant alloy CM88Y and the alloy for the protective coating of the SDP3-A blades. SDP3-A alloy was chosen as a reference sample, which has high hydrogen and corrosion resistance. The new heat-resistant alloy additionally contains such refractory metals as rhenium and tantalum, which are added to the composition of the alloy in order to increase operational characteristics while maintaining phase-structural stability. These are properties such as long-term and fatigue strength, characteristics of plasticity and strength at room and elevated temperatures. Therefore, the purpose of these studies was to determine the resistance to high-temperature salt corrosion of the developed alloy in comparison with the industrial heat-resistant nickel alloy and to evaluate the influence of alloying, hydrogen embrittlement of CM88Y and ZhS3DK alloys with different contents of chromium, boron, zirconium, hafnium, and yttrium were compared. The corrosion resistance of the materials was evaluated after crucible tests in a salt solution at a temperature of 900 °C for 30 h, according to the standard method. The corrosion resistances of alloys were determined by the mass loss, corrosion rate, and data from metallographic studies.