This work presents the development of novel gypsum board composites for advanced thermal energy storage (TES) and electromagnetic interference (EMI) shielding applications. Activated carbon (AC) derived from spent coffee with a high surface area (SBET = 1372 m2/g) was used as a shape stabilizer, while the commercial paraffin, RT18HC, was used as organic encapsulant phase change material (PCM). The AC showed a remarkable encapsulation efficiency as a shape stabilizer for PCM, with ~120.9 wt% (RT18HC), while the melting enthalpy (ΔHm) of the shape-stabilized PCM was 117.3 J/g. The performance of this PCM/carbon nanocomposite as a thermal energy storage material was examined by incorporating it into building components, such as gypsum wallboards. The microstructure of these advanced panels, their density, and their dispersion of additives were examined using X-ray microtomography. Their thermal-regulated performance was measured through a self-designed room model with a similar homemade environmental chamber that was able to create a uniform temperature environment, surrounding the test room during heating and cooling. The measurements showed that the advanced panels reduce temperature fluctuations and the indoor temperature of the room model, in comparison with normal gypsum panels, by a range of 2–5%. The investigated gypsum board composite samples showed efficient electromagnetic shielding performance in a frequency range of 3.5–7.0 GHz, reaching an EMI value of ~12.5 dB, which is adequate and required for commercial applications, when filled with PCMs.

The increasing prominence of glass-fibre-reinforced plastics (GFRPs) in the wind energy industry, due to their exceptional combination of strength, low weight, and resistance to corrosion, makes them an ideal candidate for enhancing the performance and durability of wind turbine blades. The unique properties of GFRPs not only contribute to reduced energy costs through improved aerodynamic efficiency but also extend the operational lifespan of wind turbines. By modifying the epoxy resin with carbon nanofillers, an even higher degree of performance can be achieved. In this work, graphene nanoplatelet (GNP)-enhanced GFRPs are produced through industrial methods (filament winding) and coupons are extracted and tested for their mechanical performance after harsh environmental aging in high temperature and moisture. GNPs enhance the in-plane shear strength of GFRP by 200%, while reducing their water uptake by as much as 40%.